High strength, easy to mill and excellent cost-benefit.
ADVANTAGES
✔ Stability in work, easy milling
✔ Ideal for full arches and extensive bridges
✔ High mechanical resistance and economic efficiency
FEATURES
CUBIC
Monoclinic phase content
< 15%
Sintering density
6.06 ± 0.01 g/cm³
Sintering temperature
1450 °C
Flexural strength
650 MPa
Translucency
47%
Application: Ideal for anterior restorations where aesthetics are essential. High translucency for a natural result.
SOLID
Monoclinic phase content
< 15%
Sintering density
6.09 ± 0.01 g/cm³
Sintering temperature
1530 °C
Flexural strength
1200 MPa
Translucency
41% – 43%
Application: Versatile, with a good balance between strength and translucency. Suitable for crowns and bridges in anterior and posterior areas.
VITALITY
Monoclinic phase content
< 15%
Sintering density
6.08 ± 0.01 g/cm³
Sintering temperature
1530 °C
Flexural strength: 1000 MPa
Translucency: 46%
Application: Excellent choice for restorations that require both aesthetics and strength. Ideal for aesthetic areas with structural demands.
CLASSIC
Monoclinic phase content
< 15%
Sintering density
6.09 ± 0.01 g/cm³
Sintering temperature
1530 °C
Flexural strength
1350 MPa
Translucency
37%
Application: Suitable for long structures and posterior areas that require maximum mechanical resistance. Excellent for full arches.